Degradation of sodium co-intercalation chemistry and ether-derived interphase on graphite anodes throughout calendar growing older

Energy Environ. Sci., 2024, Advance Article
DOI: 10.1039/D4EE00993B, Paper

Jiali Wang, Junyang Hu, Feiyu Kang, Dengyun Zhai
Abnormal calendar aging is found that more severe capacity loss and decreased CE appears in partially sodiated graphite anodes. The aging indicators, intercalation degradation and SEI evolution exhibited high consistency on SOC dependence.